TN55B-03
倍韌/BESTPERNE® TN55B-03
熱塑性彈性體Thermoplastic Elastomer
產品說明Product description | ||||||||
·TN55B-03是一款高性能高分子材料，與尼龍的粘接強度高。材料耐高溫。不粘模具，可快速成型。 ·TN55B-03 is a high performance polymer material, and the high bonding strength of nylon. Material resistance to high temperature. Non stick mold, can be rapid prototyping. | ||||||||
關鍵特性Key characteristic | ||||||||
1. 表面啞，手感細膩柔軟。dumb surface, exquisite and soft feeling 2. 粘接強度非常高,可粘接材質:ABS.PC PA. 3. 成型快、不粘模具。rapid molding,non-stick mold 4. 表面耐刮擦，不易起毛屑。scratch resistance on the surface,not easy to fluff | ||||||||
功能Function | ||||||||
產品應用 main application | 工具手把Tool hand | 汽車產品Automotive products | ||||||
儀器外殼Instrument housing | ||||||||
加工方法Processing method | 注塑成型Injection molding | |||||||
環(huán)保認證 Environmental certification | ROHS | REACH | EN71-3 | |||||
PAHS | ASTM-F963 | Phthalate | ||||||
顏色Color | 本色 | |||||||
氣味Smell | 少許樹脂味A little resin smell | |||||||
外型Appearance | 圓球形小顆粒Cylindrical particle，about 3mm×1.5mm | |||||||
儲藏期Storage period | 常溫下通風干燥，24個月Ventilated dry at normal temperature，about 24 months | |||||||
包裝方式Packaging method | 25公斤/袋 25kg/bag | |||||||
物理性能Physical properties | 結果Result | 單位Unit | 方法Method | 成型條件Molding condition | ||||
比重Specific gravity | 1.02 | g/cm3 | ASTM D792 | 干燥溫度Drying temp 80℃ | ||||
硬度Hardness | 55-57A | shoreA | ASTM D2240 | 干燥時間Drying time 2Hours | ||||
拉伸強度Tensile strength | 4 | Mpa | ASTM D412 | 射嘴溫度Nozzle temp 230℃ | ||||
斷裂延伸Elongation at break | 350 | % | ASTM D412 | 螺筒一段溫度Screw 1 temp 220℃ | ||||
撕裂強度Tearing strength | 17.5 | Kn/m | ASTM D624 | 螺筒二段溫度Screw 2 temp 210℃ | ||||
熔融指數Melt index | 0.6/5KG 190℃ | g/10min | ASTM D1238 | 螺筒三段溫度Screw 3 temp 200℃ | ||||
注意事項Matters need attention | ||||||||
清洗料管 Purge compound | 需使用PP或 PE清洗干凈機臺螺桿，且把機臺射嘴徹底清除干凈please make sure you that you have cleaned the machine screw with PP or PE, and put the machine nozzle thoroughly clean | |||||||
著色 Coloring
| 請選擇以PE或EVA為基材之色母，切勿使用以PVC為基材者。另外加工時請采用較高的螺桿轉速和較高的背壓，才能讓著色劑達到較好的分散效果Please select color master batch on PE or EVA material with the exception of PVC.Higher screw speed and backpressure and needed for better colorant dispersion | |||||||
回收 Recycling | 二次料（水口料）回收比率建議最多10%。 Consistent regrind usage of up to 10% is permissible | |||||||
以上數據為我公司測量之理論數據僅供參考，版權所有@惠州塑伯新材料有限公司The above data for the theory of the measurement data of our company, for your reference only. Copyright @ Huizhou SPP New Material Co., Ltd.
如需了解更多產品信息，請聯系我們：
銷售專員：
廖流愛：13922538943（微信/手機同號）
謝運英：13826903196（微信/手機同號）
李明霞：13829234372（微信/手機同號）
技術支持：
廖慈華：13602342196（微信/手機同號）
| * 聯系人： | 請?zhí)顚懩恼鎸嵭彰?/span> |
| * 手機號碼： | 請?zhí)顚懩穆撓惦娫?/span> |
| *QQ： | |
| * 采購意向描述： | |
| 請?zhí)顚?span id="rvxzxt55" class="span_b">采購的產品數量和產品描述，方便我們進行統一備貨。 | |
| 驗證碼： |
|
| 我要評論: | |
| 內 容： |
（內容最多500個漢字，1000個字符） |
| 驗證碼： | 看不清？！ |
共有-條評論【我要評論】